Morphological Evolution of Solution-Grown Cobalt-Doped ZnO Nanostructures and Their Properties
Qui Thanh Hoai Ta, Gitae Namgung, Jin-Seo Noh
文献索引：10.1016/j.cplett.2018.04.002
全文：HTML全文
摘要
It is demonstrated that the morphology of Co-doped ZnO nanostructures can be easily altered by controlling Co-doping concentration. A facile low-temperature solution method was employed for the nanosynthesis. The morphology of the nanostructures changed from nanorods to nanoparticles, and to needle-like structures as the molar ratio of Co2+ ions increased. No noticeable changes in structural and optical properties were caused by the low concentration of Co-doping, while a magnetic transition was observed. At the very low Co concentrations below 0.3 at%, the nanostructures showed diamagnetism, whereas a paramagnetic behavior was observed at a concentration of 2.5 at%.