Synergistic effects in iron-copper bimetal doped mesoporous γ-Al2O3 for Fenton-like oxidation of 4-chlorophenol: Structure, composition, electrochemical behaviors and catalytic performance

Zhuangpeng Huang, Zhiping Chen, Yuancai Chen, Yongyou Hu

文献索引：10.1016/j.chemosphere.2018.04.001

摘要

Iron-copper bimetal supported on mesoporous γ-Al2O3 with different Fe/Cu ratios was prepared via a modified evaporation-induced self-assembly method and employed to degrade 4-chlorophenol (4-CP) in a Fenton-like process. The X-ray photoelectron spectroscopy, X-ray diffraction spectrum and UV–vis diffuse reflectance spectroscopy results confirmed the co-doping of Fe2+/Fe3+ and Cu+/Cu2+ into the lattice of γ-Al2O3 through the bonds of Al O Fe and Al O Cu. With the iron and copper co-doped in γ-Al2O3, three-fold oxygen vacancies (V0) could be achieved compared with that of non-metal catalysts, which was favorable for the reduction of iron and copper species. The 1Fe3Cu-γ-Al2O3 with a Fe/Cu mass ratio of 1:3 exhibited the highest activity on Fenton-like degradation of 4-CP due to the synergistic effects of Fe and Cu by facilitating the electron transfer in the recycles of Cu+/Cu2+ and Fe2+/Fe3+ based on the results of X-ray photoelectron spectroscopy, cyclic voltammetry and electro paramagnetic resonance analysis. The utilization efficiency of H2O2 was as high as 86.0% when 4-CP almost disappeared (i.e., 99.7 percent of 0.78 mM 4-CP) at 240 min and pH 7.0, additionally, their dechlorination and TOC removal efficiencies were 92.0% and 81.6%, respectively. The catalyst also displayed a good performance after 5th cycles. Furthermore, a possible mechanism for activation of OH on the catalyst surface was also proposed.