Tissue Engineering, Part A: Tissue Engineering 2014-12-01

In vitro and in vivo studies of BMP-2-loaded PCL-gelatin-BCP electrospun scaffolds.

Bo-Ram Kim, Thuy Ba Linh Nguyen, Young-Ki Min, Byong-Taek Lee

文献索引：Tissue Eng. Part A 20(23-24) , 3279-89, (2014)

全文：HTML全文

摘要

To confirm the effect of recombinant human bone morphogenetic protein-2 (BMP-2) for bone regeneration, BMP-2-loaded polycaprolactone (PCL)-gelatin (Gel)-biphasic calcium phosphate (BCP) fibrous scaffolds were fabricated using the electrospinning method. The electrospinning process to incorporate BCP nanoparticles into the PCL-Gel scaffolds yielded an extracellular matrix-like microstructure that was a hybrid system composed of nano- and micro-sized fibers. BMP-2 was homogeneously loaded on the PCL-Gel-BCP scaffolds for enhanced induction of bone growth. BMP-2 was initially released at high levels, and then showed sustained release behavior for 31 days. Compared with the PCL-Gel-BCP scaffold, the BMP-2-loaded PCL-Gel-BCP scaffold showed improved cell proliferation and cell adhesion behavior. Both scaffold types were implanted in rat skull defects for 4 and 8 weeks to evaluate the biological response under physiological conditions. Remarkable bone regeneration was observed in the BMP-2/PCL-Gel-BCP group. These results suggest that BMP-2-loaded PCL-Gel-BCP scaffolds should be considered for potential bone tissue engineering applications.