Dental Materials 2011-05-01

Network structures of Bis-GMA/TEGDMA resins differ in DC, shrinkage-strain, hardness and optical properties as a function of reducing agent.

Adilson Y Furuse, José Mondelli, David C Watts

文献索引：Dent. Mater. 27(5) , 497-506, (2011)

全文：HTML全文

摘要

To evaluate the influence of different tertiary amines on degree of conversion (DC), shrinkage-strain, shrinkage-strain rate, Knoop microhardness, and color and transmittance stabilities of experimental resins containing BisGMA/TEGDMA (3:1wt), 0.25wt% camphorquinone, 1wt% amine (DMAEMA, CEMA, DMPT, DEPT or DABE). Different light-curing protocols were also evaluated.DC was evaluated with FTIR-ATR and shrinkage-strain with the bonded-disk method. Shrinkage-strain-rate data were obtained from numerical differentiation of shrinkage-strain data with respect to time. Color stability and transmittance were evaluated after different periods of artificial aging, according to ISO 7491:2000. Results were evaluated with ANOVA, Tukey, and Dunnett's T3 tests (α=0.05).Studied properties were influenced by amines. DC and shrinkage-strain were maximum at the sequence: CQ