Composites Part A: Applied Science and Manufacturing 2018-01-03

Enhanced Thermal Conductivity of Polyethylene/Boron Nitride Multilayer Sheets through Annealing

Shu-Ya Yang, Yan-Fei Huang, Jun Lei, Lei Zhu, Zhong-Ming Li

Index: 10.1016/j.compositesa.2017.12.031

Full Text: HTML

Abstract

Polyethylene/hexagonal boron nitride (PE/h-BN) composite sheets with enhanced thermal conductivity were fabricated through annealing a multilayered structure of alternating high density PE (HDPE)/h-BN composite and low density PE (LDPE) layers. Multilayer sheets possess a relatively low initial content filler, and after thermal annealing at 200 °C, the PE molecules in the composite layers diffused into neighboring layers. As a result, the h-BN concentration in the composite layers increased with the annealing time, resulting in the formation of thermal conduction pathways and enhancement of the final thermal conductivity. When the volume content of h-BN was 5.97 vol.%, the through-plane thermal conductivity of the annealed specimen was 1.37 W m-1K-1, which showed an enhancement of ∼180% compared to the value of the neat composite with the same content of randomly dispersed h-BN. Our work suggests that this facile method is promising for the development of high-performance thermally conductive products.

Latest Articles:

Pelletized cellulose fibres used in twin-screw extrusion for biocomposite manufacturing: Fibre breakage and dispersion

2018-04-06

[10.1016/j.compositesa.2018.04.006]

Nonlinear hyperviscoelastic modelling of intra-ply deformation behaviour in finite element forming simulation of continuously fibre-reinforced thermoplastics

2018-04-04

[10.1016/j.compositesa.2018.03.037]

Interlayer polymerization in amine-terminated macromolecular chain-grafted expanded graphite for fabricating highly thermal conductive and physically strong thermoset composites for thermal management applications

2018-04-03

[10.1016/j.compositesa.2018.04.001]

Experimental analysis of the planar compaction and preforming of unidirectional flax reinforcements using a thin paper or flax mat as binder for the UD fibers

2018-04-03

[10.1016/j.compositesa.2018.03.036]

Reduced polyaniline decorated reduced graphene oxide/polyimide nanocomposite films with enhanced dielectric properties and thermostability

2018-04-02

[10.1016/j.compositesa.2018.03.035]

More Articles...