New orientations between β′2 phase and α matrix in a Mg-Zn-Mn alloy processed by high strain rate rolling
Jimiao Jiang, Song Ni, Hongge Yan, Qin Wu, Min Song
Index: 10.1016/j.jallcom.2018.04.005
Full Text: HTML
Abstract
Strengthening precipitates in a Mg-Zn-Mn alloy, processed by high strain rate rolling, have been characterized by transmission electron microscopy. Precipitations involve a few (0001)α plates and spherical precipitates. All the precipitates have an hexagonal structure of MgZn2 and can be defined as β′2 phase. The (0001)α plates and a portion of the spherical precipitates have a common orientation relationship of [2¯110]β2'//[011¯0]α,
(0001)β2'//(0001)α and
(011¯0)β2'//(2¯110)α to α-Mg matrix. New orientation relationships (for example,
[2¯110]β2'//[011¯0]α and
(011¯5)β2'∼//(2¯110)α) between the spherical precipitates and α-Mg matrix were firstly observed, and the formation mechanism was systematically discussed.
Latest Articles:
2018-04-11
[10.1016/j.jallcom.2018.04.061]
2018-04-11
[10.1016/j.jallcom.2018.04.126]
2018-04-10
[10.1016/j.jallcom.2018.04.085]
2018-04-09
[10.1016/j.jallcom.2018.04.095]
2018-04-07
[10.1016/j.jallcom.2018.04.052]