Microporous and Mesoporous Materials 2018-04-04

Preparation and catalytic performance of Ti-MWW zeolite membrane for phenol hydroxylation

Meihua Zhu, Yongsheng Liu, Yongkang Yao, Jiamin Jiang, Fei Zhang, Zhen Yang, Zhanghui Lu, Izumi Kumakiri, Xiangshu Chen, Hidetoshi Kita

Index: 10.1016/j.micromeso.2018.04.011

Full Text: HTML

Abstract

A novel and dense tubular Ti-MWW zeolite membrane for the phenol hydroxylation was successfully prepared on mullite support by secondary hydrothermal synthesis. The ultraviolet–visible spectroscopy and fourier transform infrared spectrometer confirmed that the Ti species was thetetrahedrally coordinated state in zeolite framework. Plenty of pure phase sheet Ti-MWW zeolite crystals were fully covered on the support surface, the Ti/Si molar ratio and thickness of the Ti-MWW zeolite layer were 0.016 and 5 μm by X-ray photoelectron spectroscopy and scanning electron microscope characterization results, respectively. The membrane showed good catalytic performance for phenol hydroxylation under pervaporation condition at 323 K. The phenol conversion and dihydroxybenzene selectivity were 22.94% and 98.33%, respectively.

Latest Articles:

Enhanced lithium ion battery performance of nano/micro-size Si via combination of metal-assisted chemical etching method and ball-milling

2018-04-09

[10.1016/j.micromeso.2018.03.035]

Adsorption of pure and predicted binary (CO2:CH4) mixtures on 13X-Zeolite: Equilibrium and kinetic properties at offshore conditions

2018-04-04

[10.1016/j.micromeso.2018.04.007]

Microstructure reconstruction and impedance spectroscopy study of LiCoO2, LiMn2O4 and LiFePO4 Li-ion battery cathodes

2018-04-04

[10.1016/j.micromeso.2018.04.001]

Ammonium tagged Hoveyda-Grubbs catalysts immobilized on magnetically separable core-shell silica supports for ring-closing metathesis reactions

2018-04-04

[10.1016/j.micromeso.2018.04.002]

Characteristics of acetylene cracking on MCM-41 to form carbon materials and their exhaust emission

2018-04-04

[10.1016/j.micromeso.2018.04.006]

More Articles...