Metal Microporous Aromatic Polymers with Improved Performance for Small Gas Storage.
Xian Fu, Yindong Zhang, Shuai Gu, Yunlong Zhu, Guipeng Yu, Chunyue Pan, Zhonggang Wang, Yuehua Hu
文献索引:Chemistry 21 , 13357-63, (2015)
全文:HTML全文
摘要
A novel metal-doping strategy was developed for the construction of iron-decorated microporous aromatic polymers with high small-gas-uptake capacities. Cost-effective ferrocene-functionalized microporous aromatic polymers (FMAPs) were constructed by a one-step Friedel-Crafts reaction of ferrocene and s-triazine monomers. The introduction of ferrocene endows the microporous polymers with a regular and homogenous dispersion of iron, which avoids the slow reunion that is usually encountered in previously reported metal-doping procedures, permitting a strong interaction between the porous solid and guest gases. Compared to ferrocene-free analogues, FMAP-1, which has a moderate BET surface area, shows good gas-adsorption capabilities for H2 (1.75 wt % at 77 K/1.0 bar), CH4 (5.5 wt % at 298 K/25.0 bar), and CO2 (16.9 wt % at 273 K/1.0 bar), as well as a remarkably high ideal adsorbed solution theory CO2 /N2 selectivity (107 v/v at 273 K/(0-1.0) bar), and high isosteric heats of adsorption of H2 (16.9 kJ mol(-1) ) and CO2 (41.6 kJ mol(-1) ). © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
相关化合物
相关文献:
2015-01-01
[PLoS ONE 10 , e0131475, (2015)]
2008-04-01
[Eur. J. Med. Chem. 43 , 714-40, (2008)]
2015-05-01
[Small 11 , 2454-62, (2015)]
2015-11-09
[Chemistry 21 , 16411-20, (2015)]
2014-06-01
[J. Chromatogr. B. Analyt. Technol. Biomed. Life Sci. 960 , 1-7, (2014)]