Nanostructured hydroxyapatite as filler for methacrylate-based root canal sealers.
F M Collares, V C B Leitune, F V Rostirolla, R M Trommer, C P Bergmann, S M W Samuel
文献索引:Int. Endod. J. 45(1) , 63-7, (2012)
全文:HTML全文
摘要
To evaluate the effect of different concentrations of nanostructured hydroxyapatite on the radiopacity, flow and film thickness of an experimental root canal sealer. An experimental dual-cured root canal sealer was produced with a methacrylate-based co-monomer blend. Nanostructured hydroxyapatite/calcium tungstate solutions (ratios 10:90, 20:80, 30:70 and 40:60) were added to produce the sealer. Radiopacity was evaluated using a digital system and an aluminium step wedge (n=5). Flow and thickness tests were conducted in accordance with ISO 6876 (n=3). The data were analysed using one-way anova and Tukey's test (α=0.05). All groups had levels of radiopacity in accordance with ISO 6876. The flow of the experimental sealers was not significantly different (P=0.204). All groups had a film thickness in accordance with ISO 6876 and with no statistical difference (P = 0.654).The addition of up to 40% HA(nano) to root canal sealers did not alter their radiopacity and film thickness.© 2011 International Endodontic Journal.
相关化合物
相关文献:
2011-04-01
[Eur. J. Orthod. 33(2) , 167-73, (2011)]
1991-09-01
[Biomaterials 12(7) , 649-52, (1991)]
1995-05-01
[J. Dent. Res. 74(5) , 1162-7, (1995)]
1996-12-01
[Dent. Mater. J. 15(2) , 132-43, (1996)]
1993-04-01
[Acta Derm. Venereol. 73(2) , 126-9, (1993)]